Dead burned magnesia bricks description

1. High temperature performance and high-density
2. Easy to rapid sintering
3. Good thermal shock stability

Dead burned magnesia bricks application
The regenerative chamber for the ceramic frit kiln, sodium silicate and glass furnace
The furnace lining of iron and steel industry, such as ferroalloys furnace, metal mixer
The non-ferrous metallurgy industrial furnace lining, such as the furnace copper, lead, zinc, tin, etc
Calcining kiln, shaft kiln and tunnel kiln for refractory material industry
The lining for cement rotary kiln

Advantage of  MgO Brick

MgO brick, it is to point to magnesium stone as raw materials, the Israeli magnesium stone as the main crystal phase, MGO style content in 80% ~ 85% or more of the refractory brick. Its products are divided into two categories: Metallurgical magnesia and magnesia products. Magnesia brick is the main products of basic brick, high refractoriness, of alkaline slag and iron slag has good resistance, high refractory brick is a kind of important. Mainly used in open hearth, oxygen converter, electric furnace and non-ferrous metal smelting, etc.

TEE	Dead burned magnesia bricks
	DDMZ91	DDMZ92	DDMZ95A	DDMZ95B	DDMZ97A	DDMZ97B
MgO%≥	91	92	94.5	96	97	97.5
CaO%≤	3.0	2.5	2.0	2.0	1.8	--
SiO2≤	--	--	2.0	2.5	2.5	1.2
Normal temperature compression strength Mpa p	55	55	60	60	60	60
softening temp.C≥	1520	1540	1650	1650	1700	1700
Apparent Porosity%≤	18	18	17	18	18	16

MgO refractory  Features

Excellent performance of basic slag resistance, high refractoriness, thermal stability, anti-erosion and anti-peeling
Excellent strength of pressure bending, abrasion proof
Excellent performance of high-temperature firing, high rates of associative property, anti-erosion ability
Excellent thermal shock resistance and spalling resistance
Excellent ability of high refractoriness, anti-erosion of alkaline residue;
High temperature load of refractoriness under load. High mechanical strength
High temperature resistance excellent corrosion resistance
Resistance to spalling


It is basic refractory which the main phase is periclase. The product has such characteristics as high temperature resistance. Good slag resistance. strong corrosion resistance and steady volume in high temperature.